ZM-30 |
ZM-33 |
ZM-37 |
| Al2O3 |
42-47% |
42-47% |
42-47% |
| SiO2 |
16-20% |
16-20% |
16-20% |
| ZrO2 |
30%
min |
33%
min |
37%
min |
| Volume
density |
3.5
g/cc min |
3.6
g/cc min |
3.6
g/cc min |
| Apparent
Porosity |
3%
max |
3%
max |
3%
max |
| Baddeleyite
phase |
29-32% |
33-35% |
36-38% |
| Croundum
phase |
5%
max |
5%
max |
5%
max |
| Mullite
phase |
53%
min |
51%
min |
50%
min |
| Glass
phase |
5%
max |
5%
max |
5%
max |
Brand
Property |
AZS-1 |
AZS-2 |
AZS-3 |
GRIT>0.1mm |
FINE¡Ü0.1mm |
GRIT>0.1mm |
FINE¡Ü0.1mm |
GRIT>0.1mm |
FINE¡Ü0.1mm |
| Chemical
Composition |
Al2O3%
|
40-46 |
40-46 |
46¡À3 |
46¡À3 |
46¡À3 |
46¡À3 |
| SiO2%
|
13-19 |
13-19 |
18¡À2 |
18¡À2 |
18¡À2 |
18¡À2 |
| ZrO2% |
¡Ý34 |
¡Ý34 |
37¡À3 |
37¡À3 |
¡Ý36 |
¡Ý36 |
| Fe2O3%
¡Ü |
0.3 |
0.3 |
0.15 |
0.15 |
0.1 |
0.1 |
| Na2O+Ka2O%
¡Ü |
0.3 |
0.3 |
0.3 |
0.3 |
0.3 |
0.3 |
| Physical
Porperty |
Magnetic
Matter% ¡Ü |
0.05 |
0.1 |
0.05 |
0.1 |
0.05 |
0.1 |
| Apparent
Porosity% ¡Ü |
3.0 |
3.0 |
3.0 |
| Bulk
Density g/cm3¡Ý |
3.60 |
3.60 |
3.60 |
| calcination@1500¡æ |
|
|
Fleckless |
| chemical
composition(%) |
Al2O3 |
42-50 |
ZrO2 |
33-37 |
SiO2 |
16-20 |
| crystalline
phase(%) |
mullite
crystalline phase |
50-55 |
zirconium
crystalline phase |
30-33 |
croundum
crystalline phase |
¡Ü5 |
glass
crystalline phase |
¡Ü5 |
| bulk
density (g/cm3) |
¡Ý3.60 |
| apparent
porosity(%) |
¡Ü3 |